| IC Leadframes, Connectors, Springs, Thermostat Contacts, Electrical Components |
|
 |
Good combination of strength and electrical conductivity with good bend formability.
|
|
High corrosion resistance.
|
| Fe |
P |
Zn |
Cu |
| 2.35 |
0.07 |
0.12 |
Bal. |
|
| (wt.%) |
 *
|
Density at 20 |
g/cm3 |
8.91 |
|
| Modulus of Elasticity |
kN/mm2 |
121 |
|
| Elecrical Resistivity |
   m |
2.54 10-2 |
|
| Thermal Conductivity at 20 |
W/(mK) |
2.62102 |
|
| Coefficient of Thermal Expansion at 20-300 |
10-6 |
17.4 |
|
| Melting Point Liquidus |
|
1089 |
|
| Melting Point Solidus |
|
1084 |
|
| * Reference value only. |
| Temper |
Tensile Strength
N/mm2 |
Elongation*
% |
Hardness*
HV |
Electrical Conductivity
%IACS |
| 1/2H |
365-434 |
6min |
115-135 |
60min |
| H |
413-482 |
3min |
125-145 |
60min |
| EH |
461-503 |
2min |
135-150 |
60min |
| SH |
482-523 |
- |
140-155 |
60min |
| ESH |
503-551 |
- |
145-160 |
60min |
| SSH |
 551 |
- |
155 |
50min |
| SH(RA) |
482-524 |
4min |
140-155 |
60min |
| EX-SPR(RA) |
531-573 |
5min |
150-165 |
60min |
|
|
* Reference value only.
|
|
The specifications shown above are those as of June, 2006.
The specifications are subject to change without notice. |
|